Production Description:
High density polyethylene geomembranes HDPE are used as a waterproof barrier for all types of hydraulic work like water reservoirs for agriculture, canals, treatment plants, settling ponds, evaporation ponds, farms, golf courses etc
This type of polyethylene geomembranes are used in projects related to the environment as a barrier to contain liquid or solid contaminants such as waste landfills, leachate, slurry, mining waste, protection against leaks in petrochemical industries, airports, harbours, etc
Product is used as well in civil engineering in railway constructions, roads, walls, tunnels, pavements, etc.
The product has excellent temperature adaptability, weldability, tolerance and aging resistance, chemical corrosion resistance, environmental stress cracking resistance and anti pierce performance. It's especially suitable for underground engineering, mining engineering, sewage and waste residue treatment plant as impermeable material.
With three layer extrusion production method, making geomembrane in good quality and high yield strength, product width,length and color can be customized.
Product specifications
| Thickness | 0.25mm | 0.35mm | 0.5mm | 0.75mm | 1.0mm | 1.25mm | 1.5mm | 2.0mm |
| Density g/m2 | ≥0.94 | |||||||
| Tensile yield strength (N/mm) | 3.75 | 5 | 7.5 | 11 | 15 | 18 | 22 | 29 |
| Tensile breaking strength (N/mm) | 6.75 | 19 | 13.5 | 20 | 27 | 33 | 40 | 53 |
| Elongation at yield(%) | ≥12 | |||||||
| Elongation at break(%) | ≥700 | |||||||
| Puncture strength(N) | 80 | 150 | 160 | 240 | 320 | 400 | 480 | 640 |
| Angle tear load | 31.25 | 45 | 62.5 | 93 | 125 | 160 | 190 | 250 |
| Carbon black content(%) | 2.0-3.0 | |||||||
| 85℃ aging after 90 days high pressure | 55 | |||||||
| Properties | Test | Test Value | Testing Frequency | |||||||
| Method | 30 mils | 40 mils | 50 mils | 60 mils | 80 mils | 100 mils | 120 mils | (minimum) | ||
| Thickness (min. ave.) | D5199 | nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Per roll | |
| · lowest individual of 10 values | -10% | -10% | -10% | -10% | -10% | -10% | -10% | |||
| Density mg/l (min.) | D 1505/D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 200,000 lb | |
| Tensile Properties (1) (min. ave.) | D 6693 | 20,000 lb | ||||||||
| Yield strength | Type IV | 63 lb/in. | 84 lb/in. | 105 lb/in. | 126 lb/in. | 168 lb/in. | 210 lb/in. | 252 lb/in. | ||
| Break strength | 114 lb/in. | 152 lb/in. | 190 lb/in. | 228 lb/in. | 304 lb/in. | 380 lb/in. | 456 lb/in. | |||
| Yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | |||
| Break elongation | 700% | 700% | 700% | 700% | 700% | 700% | 700% | |||
| Tear Resistance (min. ave.) | D 1004 | 21 lb | 28 lb | 35 lb | 42 lb | 56 lb | 70 lb | 84 lb | 45,000 lb | |
| Puncture Resistance (min. ave.) | D 4833 | 54 lb | 72 lb | 90 lb | 108 lb | 144 lb | 180 lb | 216 lb | 45,000 lb | |
| Stress Crack Resistance (2) | D5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI-GM10 | |
| (App.) | ||||||||||
| Carbon Black Content (range) | D 4218 (3) | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 20,000 lb | |
| Carbon Black Dispersion | D 5596 | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | 45,000 lb | |
| Oxidative Induction Time (OIT) (min. ave.) (5) | 200,000 lb | |||||||||
| (a) | Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | |
| — or — | ||||||||||
| (b) High Pressure OIT | D 5885 | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | ||
| Oven Aging at 85°C (5), (6) | D 5721 | |||||||||
| (a) Standard OIT (min. ave.) - % retained after 90 days | D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 90 days | D 5885 | 80% | 80% | 80% | 80% | 80% | 80% | 80% | ||
| UV Resistance (7) | D 7238 | |||||||||
| (a) Standard OIT (min. ave.) | D 3895 | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (9) | D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | ||
Appications
Thickness for different project
1, Aquaculture (including fish pond, shrimp pond, seaweed farming etc. )
normally use 0.25mm~0.5mm
2, Agriculture( including lotus farming, reservoir, drinking water tank, irrigation system etc.) normally use 0.5mm~1.0mm
3, Landscape (including artificial lake, river, slop protection, greening waterproof etc.) normally use 0.5mm~1.0mm
4, Water conservancy ( including dam anti-seepage, strengthen etc.)
normally use 0.75mm~1.5mm
5, Roof anti-seepage ( roof planting, roof waterproof, roof garden waterproof etc.)
normally use 0.5mm~1.0mm
6, Underground anti-seepage ( including traffic, subway and roadway’s foundation strengthen, workshop waterproof)
normally use 0.5mm~1.0mm
7, Environmental protection (including landfill, sewage treatment work, power regulating reservoir, industrial and hospital solid waste)
normally use 1.0mm~2.0mm
8, Mining (including Washing tank, ash yard, dissolution tank, sedimentation tank, bottom anti-seepage of tailings etc.)
normally use 1.0mm~2.0mm