Quick Detail:
Advantage:
1. Good impermeable performance: vapor permeability coefficience K<=1.0*10-13g.cm/(cm2.s.Pa)
2. High strength: breaking tensile strength >=28MP
3. Service life: up to about 100 years.
4. Lower temperature-resistance: cold brittleness temperatures -70C.
5. Corrosion resistance: capability to resist more than 80 species of strong acid, alkali, etc.
6. Non-toxic: harmless, pollution-free, widely used in water-drinking proiects abroad.
7. Excellent economic benefit: lower cost and investment.
8. Good welding performance: high welding strength.
Product Parameter
| Material | high density polyethylene |
| Thickness | from 0.25mm to 3.0mm, or according customers' requirement |
| Color | green, balck, white and transparent |
| Length | from 50m to 200m & customer ' s requirement |
| Width | from 1.0m to 8.0m, or according customers' requirement |
| Package | woven bag, or according customers' requirement |
| Surface | Smooth |
| Production Standard | ISO, GRI,ASTM,GB |
| Shipping Marks | support |
| Thickness | 0.25mm | 0.35mm | 0.5mm | 0.75mm | 1.0mm | 1.25mm | 1.5mm | 2.0mm |
| Density g/m2 | ≥0.94 | |||||||
| Tensile yield strength (N/mm) | 3.75 | 5 | 7.5 | 11 | 15 | 18 | 22 | 29 |
| Tensile breaking strength (N/mm) | 6.75 | 13.5 | 19 | 20 | 27 | 33 | 40 | 53 |
| Elongation at yield(%) | ≥12 | |||||||
| Elongation at break(%) | ≥700 | |||||||
| Puncture strength(N) | 80 | 150 | 160 | 240 | 320 | 400 | 480 | 640 |
| Angle tear load | 31.25 | 45 | 62.5 | 93 | 125 | 160 | 190 | 250 |
| Carbon black content(%) | 2.0-3.0 | |||||||
| 85℃ aging after 90 days high pressure | 55 | |||||||
Data
| Properties | Test | Test Value | Testing Frequency | |||||||
| Method | 30 mils | 40 mils | 50 mils | 60 mils | 80 mils | 100 mils | 120 mils | (minimum) | ||
| Thickness (min. ave.) | D5199 | nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Per roll | |
| Lowest individual of 10 values | -10% | -10% | -10% | -10% | -10% | -10% | -10% | |||
| Density mg/l (min.) | D 1505/D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 200,000 lb | |
| Tensile Properties (1) (min. ave.) | D 6693 | 20,000 lb | ||||||||
| Yield strength | Type IV | 63 lb/in. | 84 lb/in. | 105 lb/in. | 126 lb/in. | 168 lb/in. | 210 lb/in. | 252 lb/in. | ||
| Break strength | 114 lb/in. | 152 lb/in. | 190 lb/in. | 228 lb/in. | 304 lb/in. | 380 lb/in. | 456 lb/in. | |||
| Yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | |||
| Break elongation | 700% | 700% | 700% | 700% | 700% | 700% | 700% | |||
| Tear Resistance (min. ave.) | D 1004 | 21 lb | 28 lb | 35 lb | 42 lb | 56 lb | 70 lb | 84 lb | 45,000 lb | |
| Puncture Resistance (min. ave.) | D 4833 | 54 lb | 72 lb | 90 lb | 108 lb | 144 lb | 180 lb | 216 lb | 45,000 lb | |
| Stress Crack Resistance (2) | D5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI-GM10 | |
| (App.) | ||||||||||
| Carbon Black Content (range) | D 4218 (3) | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 20,000 lb | |
| Carbon Black Dispersion | D 5596 | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | 45,000 lb | |
| Oxidative Induction Time (OIT) (min. ave.) (5) | 200,000 lb | |||||||||
| (a) | Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | |
| — or — | ||||||||||
| (b) High Pressure OIT | D 5885 | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | ||
| Oven Aging at 85°C (5), (6) | D 5721 | |||||||||
| (a) Standard OIT (min. ave.) - % retained after 90 days | D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 90 days | D 5885 | 80% | 80% | 80% | 80% | 80% | 80% | 80% | ||
| UV Resistance (7) | D 7238 | |||||||||
| (a) Standard OIT (min. ave.) | D 3895 | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (9) | D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | ||
Application:
1. Environmental protection and sanitation (such as domestic waste landfills, sewage treatment, toxic and hazardous substance disposal sites, hazardous goods warehouses, industrial waste, construction and blasting waste, etc.)
2. Water conservancy (such as anti-seepage, plugging, reinforcement of dams of rivers, lakes and reservoirs, anti-seepage of canals, vertical core walls, slope protection, etc.)
3. Municipal engineering (subway, underground engineering of buildings and roof cisterns, seepage prevention of roof gardens, lining of sewage pipes, etc.)
4. Gardens (artificial lakes, ponds, pond linings of golf courses, slope protection, etc.)
5. Petrochemical (chemical plants, refineries, oil storage tanks in gas stations, seepage prevention, chemical reaction tanks, sedimentation tank linings, secondary linings, etc.)
6. Mining (washing tank, heap leaching tank, ash yard, dissolution tank, sedimentation tank, storage yard, bottom lining anti-seepage of tailings pond, etc.)
7. otus root planting (lotus root planting, anti-seepage of lotus pond, water storage pond, anti-seepage of irrigation system)
8. Aquaculture (lining of fish ponds, shrimp ponds, sea cucumber circle slope protection, etc.)
9. Salt industry (salt field crystallization pond, brine pond cover, salt film, salt pond plastic film)
Package:
Packaging Details:
Neutral package of Pond Liner Material
Roll Size: 5.8m*50m 100m
Or packed according to customers' requirements such as mark the company Logo
As example:
Specification 20ft container 40ft container
0.2mm size: 5.8m*300m 20GP 58rolls 10092 sqm