Production Description:
Our anti-seepage HDPE geomembrane is made from 97.5% high density polyethylene (HDPE) and 2.5% Carbon black/anti-aging agent/anti-oxygen/UV absorbent/stabilizer and other accessory, which is widely used for fish pond, solid waste containment and water containment environment and mining environment. Product is made of best quality high density polyethylene (HDPE) with specially formulated and original polyethylene resin, combined with specified quantity carbon black, antioxidant, anti-aging agent and UV resistance components, which contributes to its excellent resistance to UV radiation and being suitable for different conditions.
HDPE anti-seepage composite geomembrane with rough surface is a new type of anti-seepage material. Single rough surface and double rough surface increase friction coefficient and anti-skid function, which is more suitable for steep slope and vertical anti-seepage and provides engineering stability.
It has excellent temperature adaptability, weldability, tolerance and aging resistance, chemical corrosion resistance, environmental stress cracking resistance and anti pierce performance. It's especially suitable for underground engineering, mining engineering, sewage and waste residue treatment plant as impermeable material.
Product Parameter
| Thickness | 0.25mm | 0.35mm | 0.5mm | 0.75mm | 1.0mm | 1.25mm | 1.5mm | 2.0mm |
| Density g/m2 | ≥0.94 | |||||||
| Tensile yield strength (N/mm) | 3.75 | 5 | 7.5 | 11 | 15 | 18 | 22 | 29 |
| Tensile breaking strength (N/mm) | 6.75 | 19 | 13.5 | 20 | 27 | 33 | 40 | 53 |
| Elongation at yield(%) | ≥12 | |||||||
| Elongation at break(%) | ≥700 | |||||||
| Puncture strength(N) | 80 | 150 | 160 | 240 | 320 | 400 | 480 | 640 |
| Angle tear load | 31.25 | 45 | 62.5 | 93 | 125 | 160 | 190 | 250 |
| Carbon black content(%) | 2.0-3.0 | |||||||
| 85℃ aging after 90 days high pressure | 55 | |||||||
| Properties | Test | Test Value | Testing Frequency | |||||||
| Method | 30 mils | 40 mils | 50 mils | 60 mils | 80 mils | 100 mils | 120 mils | (minimum) | ||
| Thickness (min. ave.) | D5199 | nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Per roll | |
| · lowest individual of 10 values | -10% | -10% | -10% | -10% | -10% | -10% | -10% | |||
| Density mg/l (min.) | D 1505/D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 200,000 lb | |
| Tensile Properties (1) (min. ave.) | D 6693 | 20,000 lb | ||||||||
| Yield strength | Type IV | 63 lb/in. | 84 lb/in. | 105 lb/in. | 126 lb/in. | 168 lb/in. | 210 lb/in. | 252 lb/in. | ||
| Break strength | 114 lb/in. | 152 lb/in. | 190 lb/in. | 228 lb/in. | 304 lb/in. | 380 lb/in. | 456 lb/in. | |||
| Yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | |||
| Break elongation | 700% | 700% | 700% | 700% | 700% | 700% | 700% | |||
| Tear Resistance (min. ave.) | D 1004 | 21 lb | 28 lb | 35 lb | 42 lb | 56 lb | 70 lb | 84 lb | 45,000 lb | |
| Puncture Resistance (min. ave.) | D 4833 | 54 lb | 72 lb | 90 lb | 108 lb | 144 lb | 180 lb | 216 lb | 45,000 lb | |
| Stress Crack Resistance (2) | D5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI-GM10 | |
| (App.) | ||||||||||
| Carbon Black Content (range) | D 4218 (3) | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 20,000 lb | |
| Carbon Black Dispersion | D 5596 | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | 45,000 lb | |
| Oxidative Induction Time (OIT) (min. ave.) (5) | 200,000 lb | |||||||||
| (a) | Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | |
| — or — | ||||||||||
| (b) High Pressure OIT | D 5885 | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | ||
| Oven Aging at 85°C (5), (6) | D 5721 | |||||||||
| (a) Standard OIT (min. ave.) - % retained after 90 days | D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 90 days | D 5885 | 80% | 80% | 80% | 80% | 80% | 80% | 80% | ||
| UV Resistance (7) | D 7238 | |||||||||
| (a) Standard OIT (min. ave.) | D 3895 | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (9) | D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | ||
Appications
HDPE Geomembrane recommend thickness of application
1, Aquaculture (including fish pond, shrimp pond, seaweed farming etc. )
normally use 0.25mm~0.5mm
2, Agriculture( including lotus farming, reservoir, drinking water tank, irrigation system etc.) normally use 0.5mm~1.0mm
3, Landscape (including artificial lake, river, slop protection, greening waterproof etc.) normally use 0.5mm~1.0mm
4, Water conservancy ( including dam anti-seepage, strengthen etc.)
normally use 0.75mm~1.5mm
5, Roof anti-seepage ( roof planting, roof waterproof, roof garden waterproof etc.)
normally use 0.5mm~1.0mm
6, Underground anti-seepage ( including traffic, subway and roadway’s foundation strengthen, workshop waterproof)
normally use 0.5mm~1.0mm
7, Environmental protection (including landfill, sewage treatment work, power regulating reservoir, industrial and hospital solid waste)
normally use 1.0mm~2.0mm
8, Petrochemical ((including refinery plant, chemical reaction camera, inner liners of setting tank, secondary liner etc. )
normally use 0.5mm~1.0mm
9, Mining (including Washing tank, ash yard, dissolution tank, sedimentation tank, bottom anti-seepage of tailings etc.)
normally use 1.0mm~2.0mm