| Place of Origin: | Luan, China |
|---|---|
| Brand Name: | Wanshengli |
| Certification: | ISO, GB, BV, SASO, SONCAP |
| Model Number: | Customized |
| Minimum Order Quantity: | 1160sqm |
| Price: | 0.49USD~3.5USD per sqm |
| Packaging Details: | Plastic bags or as your request |
| Delivery Time: | As per your quantity |
| Payment Terms: | L/C, D/P, T/T, Western Union, MoneyGram |
| Supply Ability: | 50000 sqm per day |
| Features: | Anti-uv Hdpe Pond Liner,aging Resistence,waterproof,UV Resistence | Product Main Material: | Polyethylene, HDPE |
|---|---|---|---|
| Product Color: | Black | Product Packing: | Woven Plastic Bag |
| Description: | Chemical Stabilized Hdpe Plastic Membrane | Length: | 50m |
| Width: | 5.8m | Thickness: | 0.25mm To 2.0mm |
| Certificate: | ISO, GB, BV, SASO, SONCAP | Sample: | Support |
| High Light: | geomembrana hdpe 30 mils Liner,Polyethylene geomembrana hdpe 30 mils,Polyethylene geomembrana 30 mils |
||
Quick Detail:
Product Parameter
| Thickness | 0.25mm | 0.35mm | 0.5mm | 0.75mm | 1.0mm | 1.25mm | 1.5mm | 2.0mm |
| Density g/m2 | ≥0.94 | |||||||
| Tensile yield strength (N/mm) | 3.75 | 5 | 7.5 | 11 | 15 | 18 | 22 | 29 |
| Tensile breaking strength (N/mm) | 6.75 | 13.5 | 19 | 20 | 27 | 33 | 40 | 53 |
| Elongation at yield(%) | ≥12 | |||||||
| Elongation at break(%) | ≥700 | |||||||
| Puncture strength(N) | 80 | 150 | 160 | 240 | 320 | 400 | 480 | 640 |
| Angle tear load | 31.25 | 45 | 62.5 | 93 | 125 | 160 | 190 | 250 |
| Carbon black content(%) | 2.0-3.0 | |||||||
| 85℃ aging after 90 days high pressure | 55 | |||||||
Date
| Properties | Test | Test Value | Testing Frequency | |||||||
| Method | 30 mils | 40 mils | 50 mils | 60 mils | 80 mils | 100 mils | 120 mils | (minimum) | ||
| Thickness (min. ave.) | D5199 | nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Nom. | Per roll | |
| Lowest individual of 10 values | -10% | -10% | -10% | -10% | -10% | -10% | -10% | |||
| Density mg/l (min.) | D 1505/D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 200,000 lb | |
| Tensile Properties (1) (min. ave.) | D 6693 | 20,000 lb | ||||||||
| Yield strength | Type IV | 63 lb/in. | 84 lb/in. | 105 lb/in. | 126 lb/in. | 168 lb/in. | 210 lb/in. | 252 lb/in. | ||
| Break strength | 114 lb/in. | 152 lb/in. | 190 lb/in. | 228 lb/in. | 304 lb/in. | 380 lb/in. | 456 lb/in. | |||
| Yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | |||
| Break elongation | 700% | 700% | 700% | 700% | 700% | 700% | 700% | |||
| Tear Resistance (min. ave.) | D 1004 | 21 lb | 28 lb | 35 lb | 42 lb | 56 lb | 70 lb | 84 lb | 45,000 lb | |
| Puncture Resistance (min. ave.) | D 4833 | 54 lb | 72 lb | 90 lb | 108 lb | 144 lb | 180 lb | 216 lb | 45,000 lb | |
| Stress Crack Resistance (2) | D5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI-GM10 | |
| (App.) | ||||||||||
| Carbon Black Content (range) | D 4218 (3) | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 2.0-3.0% | 20,000 lb | |
| Carbon Black Dispersion | D 5596 | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | note (4) | 45,000 lb | |
| Oxidative Induction Time (OIT) (min. ave.) (5) | 200,000 lb | |||||||||
| (a) | Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | |
| — or — | ||||||||||
| (b) High Pressure OIT | D 5885 | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | ||
| Oven Aging at 85°C (5), (6) | D 5721 | |||||||||
| (a) Standard OIT (min. ave.) - % retained after 90 days | D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 90 days | D 5885 | 80% | 80% | 80% | 80% | 80% | 80% | 80% | ||
| UV Resistance (7) | D 7238 | |||||||||
| (a) Standard OIT (min. ave.) | D 3895 | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | N.R. (8) | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (9) | D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | ||
Application: