Anti Slip HDPE Textured Geomembrane Rough Surface Geomembrane Construction Material
HDPE Textured Geomembrane
Quick Detail:
Factory directly sell the impermeable synthetic membrane liner and geotechnical engineering materials which are widely used for solid waste containment, mining and water containment applications.
Our HDPE textured geomembrane with rough surface is a new type of anti-seepage material. Single rough surface and double rough surface increase friction coefficient and anti-skid function, which is more suitable for steep slope and vertical anti-seepage and providing engineering stability.
HDPE textured geomembrane product is made from 97.5% high density polyethylene (HDPE) and 2.5% Carbon black/anti-aging agent/anti-oxygen/UV absorbent/stabilizer and other accessory, which is widely used for fishpond, landfill project and water containment environment and mining environment. Anti-seepage HDPE texture geomembrane is made of best quality high density polyethylene (HDPE) with specially formulated and original polyethylene resin, combined with specified quantity carbon black, antioxidant, anti-aging agent and UV resistance components, which contributes to its excellent resistance to UV radiation and being suitable for different conditions.
Wanshengli Brand hdpe textured geomembrane has excellent temperature adaptability, weldability, tolerance and aging resistance, chemical corrosion resistance, environmental stress cracking resistance and anti pierce performance. Therefore, it is especially suitable for underground engineering, mining engineering, sewage and waste residue treatment plant as impermeable materials.
Advantages:
Product Parameter
Properties |
Test | Test Value | Testing | |||||||
| Method | Frequency | |||||||||
| 30 mils | 40 mils | 50 mils | 60 mils | 80 mils | 100 mils | 120 mils | (minimum) | |||
| Thickness mils (min. ave.) | D 5994 | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | nom. (-5%) | per roll | |
| · | lowest individual for 8 out of 10 values | -10% | -10% | -10% | -10% | -10% | -10% | -10% | ||
| · | lowest individual for any of the 10 values | -15% | -15% | -15% | -15% | -15% | -15% | -15% | ||
| Asperity Height mils (min. ave.) (1) | D 7466 | 10 mil | 10 mil | 10 mil | 10 mil | 10 mil | 10 mil | 10 mil | every 2nd roll (2) | |
| Density (min. ave.) | D 1505/D 792 | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 0.940 g/cc | 200,000 lb | |
| Tensile Properties (min. ave.) (3) | D 6693 | 20,000 lb | ||||||||
| · | yield strength | Type IV | 63 lb/in. | 84 lb/in. | 105 lb/in. | 126 lb/in. | 168 lb/in. | 210 lb/in. | 252 lb/in. | |
| · | break strength | 45 lb/in. | 60 lb/in. | 75 lb/in. | 90 lb/in. | 120 lb/in. | 150 lb/in. | 180 lb/in. | ||
| · | yield elongation | 12% | 12% | 12% | 12% | 12% | 12% | 12% | ||
| · | break elongation | 100% | 100% | 100% | 100% | 100% | 100% | 100% | ||
| Tear Resistance (min. ave.) | D 1004 | 21 lb | 28 lb | 35 lb | 42 lb | 56 lb | 70 lb | 84 lb | 45,000 lb | |
| Puncture Resistance (min. ave.) | D 4833 | 45 lb | 60 lb | 75 lb | 90 lb | 120 lb | 150 lb | 180 lb | 45,000 lb | |
| Stress Crack Resistance (4) | D 5397 | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | 300 hr. | per GRI GM10 | |
| (App.) | ||||||||||
| Carbon Black Content (range) | D 4218 (5) | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 2.0-3.0 % | 20,000 lb | |
| Carbon Black Dispersion | D 5596 | note (6) | note (6) | note (6) | note (6) | note (6) | note (6) | note (6) | 45,000 lb | |
| Oxidative Induction Time (OIT) (min. ave.) (7) | 200,000 lb | |||||||||
| (a) Standard OIT | D 3895 | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | 100 min. | ||
| — or — | ||||||||||
| (b) High Pressure OIT | D 5885 | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | 400 min. | ||
| Oven Aging at 85°C (7), (8) | D 5721 | |||||||||
| (a) Standard OIT (min. ave.) - % retained after 90 days | D 3895 | 55% | 55% | 55% | 55% | 55% | 55% | 55% | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 90 days | D 5885 | 80% | 80% | 80% | 80% | 80% | 80% | 80% | ||
| UV Resistance (9) | D 7238 | |||||||||
| (a) Standard OIT (min. ave.) | D 3895 | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | N.R. (10) | per each | |
| — or — | formulation | |||||||||
| (b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (11) | D 5885 | 50% | 50% | 50% | 50% | 50% | 50% | 50% | ||
| Item | Parameter | |||||
| Thickness (mm) | 1.0mm | 1.25mm | 1.5mm | 2.0mm | 2.5mm | 3.0mm |
| Coarse height(mm) | 0.25 | |||||
| Minimum Density ( g/cm3) | 0.94 | |||||
| Break strength (N/mm) | ≧10 | ≧13 | ≧16 | ≧21 | ≧26 | ≧32 |
| Elongation at break (%) | 100 | |||||
| Angle tear load (N) | ≧125 | ≧156 | ≧187 | ≧249 | ≧311 | ≧374 |
| Puncture strength (N) | ≧267 | ≧333 | ≧400 | ≧534 | ≧667 | ≧800 |
| Environmental stress cracking resistance hr |
300 |
|||||
| Carbon black content (%) | 2.0-3.0 | |||||
| Size Stability(%) | ±2 | |||||
HDPE Geomembrane recommend thickness of application
Package